dc.creatorSILVA, Gustavo Souza de Alencar e-
dc.creator.Latteshttp://lattes.cnpq.br/9615996877430479por
dc.contributor.advisor1RAMOS, Alfeu Saraiva-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/4959152343828058por
dc.contributor.referee1STRECKER, Kurt-
dc.contributor.referee2GUNNEWUIEK, Rodolfo Foster Klein-
dc.date.accessioned2018-01-05T19:58:15Z-
dc.date.issued2016-12-15-
dc.identifier.citationSILVA, Gustavo Souza de Alencar e. Sinterização por SPS de pós de W-C-CO-B preparados por moagem de alta energia. 2016. 98 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Alfenas, Poços de Caldas, MG, 2016.por
dc.identifier.urihttps://bdtd.unifal-mg.edu.br:8443/handle/tede/1057-
dc.description.resumoOs carbetos de tungstênio com matriz de cobalto são uns dos mais antigos produtos comerciais da metalurgia do pó. Estes compósitos são usados para diferentes aplicações dentre as quais se destacam a fabricação de componentes de corte e abrasivos. Tais materiais são constituídos por partículas de carbeto de tungstênio e cobalto metálico ligados pela sinterização via fase líquida e podem ser produzidos por reações químicas convencionais. As técnicas de moagem de alta energia são amplamente utilizadas para a síntese de compostos cerâmicos. O presente trabalho visou a realização de estudos de moagem de alta energia e de sinterização de misturas de pós de carbeto de tungstênio dopados com cobalto e boro. A etapa de moagem das misturas de pós elementares de W-50C (%-at.) foi realizada em um moinho de bolas planetário Fritsch P-5 utilizando esferas (10 mm de diâmetro) e vaso de WC-Co, velocidade de 200 rpm e uma relação de massas esferas-pós de 10:1. O tempo de moagem foi variado: 20, 60, 180 e 600 min. Na sequência, os pós de Co e de B foram misturados com os pós moídos de W-50C (%-at) e processados em um moinho Spex por 5 min. Seguindo, os materiais foram sinterizados em atmosfera controlada à 1450oC para a obtenção de corpos cilíndricos com altura de 1-3 mm e diâmetro de 10 mm. Os pós-moídos e os produtos sinterizados foram avaliados com o auxílio das técnicas de difração de raios X (DRX), microscopia eletrônica de varredura (MEV), espectrometria por dispersão de energia (EDS) e ensaios mecânicos (compressão diametral e dureza Vickers). Picos de carbono desapareceram após 180 min de moagem, enquanto que o pico principal do tungstênio foi deslocado para a direção de menores ângulos de difração em pós de W-50C moídos por 600 min. Ainda, os picos de tungstênio foram alargados e tiveram suas intensidades reduzidas em misturas de pós de W-50C moídos por 600 min, sugerindo que os átomos de carbono ficaram dissolvidos na estrutura cristalina do tungstênio para formar soluções sólidas supersaturadas. Amostras densas (> 96% da massa específica teórica) com microestruturas formadas pela fase WC como matriz além de precipitados ricos em boro e de W2C foram obtidos após spark plasma sintering das misturas de pós contendo adição de boro. As amostras sinterizadas apresentaram valores de dureza Vickers entre 1841 HV e 2191 HV, as quais foram mais pronunciadas para as cerâmicas mais ricas em boro. Similarmente à cerâmica convencional de WC-6Co, nenhum efeito foi encontrado sobre a adição de boro no módulo elástico das cerâmicas avaliadas, as quais ficaram próximas de 500 GPa. Ao contrário, a resistência compressiva das cerâmicas de WC-6Co contendo adição de boro ficou inferior a 500 MPa.por
dc.description.abstractTungsten carbides in cobalt matrix are one of the earliest commercial products of powder metallurgy. These composites are used for different applications among which are highlighted the manufacture of cutting components and abrasives. These composites consist of tungsten carbide and metallic cobalt particles bound by sintering through the liquid phase and they can be produced by conventional chemical reactions. Mechanical alloying techniques are widely used for the synthesis of ceramic compounds. The present work aims to perform studies of mechanical alloying and sintering of powder mixtures of tungsten carbide doped with cobalt (6 wt.-%) and boron (0.2 and 0.5 at.%). Ball milling of W-50C (at.-%) elemental powder mixtures was performed in a planetary Fritsch P-5 ball mill using WC-Co balls (10 mm diameter) and vial (500 mL), rotary speed of 200 rpm, and a ball-to-powder weight ratio of 10:1. The milling time was varied: 20, 60, 180 and 600 minutes. Following, the powders of Co and B were mixed for 5 min in a Spex mill together the previous mechanically alloyed W-50C (at.-%) powders. Afterwards, the as-milled powders were consolidated by spark plasma sintering (SPS) at 1450°C under controlled atmosphere to obtain cylindrical bodies with height of 1-3 mm and 10 mm diameter. The as-milled powders and sintered products were evaluated using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), and mechanical tests (diametrical compression and Vickers hardness). Peaks of carbon disappeared after milling for 180 min whereas the major W peak was shifted toward the lower diffraction angles in W-50C powders milled for 600 min. In addition, the peaks of W were broadened and their intensities reduced after milling for 600 min, suggesting that the carbon atoms were dissolved into the W lattice in order to form supersaturated solid solutions. SPS process of mechanically alloyed W-50C powders containing Co and B produced dense samples (> 96% of theorical specific mass) which presented microstructures formed by the WC phase as matrix beside the B-rich and W2C precipitates. SPS samples presented Vickers hardness values between 1841 HV and 2191 HV which were more pronounced for B-richer ceramics. For the evaluated ceramics, no effect of boron addition on the elastic module was found, which were close to 500 GPa. On the other hand, the compressive strenght of W-50C ceramics containing Co and B addition were lower than 500 MPa.eng
dc.description.provenanceSubmitted by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2018-01-03T20:01:02Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação de Mestrado_Gustavo Souza de Alencar e Silva.pdf: 4199856 bytes, checksum: 248a84b110ca0ac9a1ec5f9375ac6121 (MD5)eng
dc.description.provenanceApproved for entry into archive by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2018-01-05T19:57:57Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação de Mestrado_Gustavo Souza de Alencar e Silva.pdf: 4199856 bytes, checksum: 248a84b110ca0ac9a1ec5f9375ac6121 (MD5)eng
dc.description.provenanceApproved for entry into archive by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2018-01-05T19:58:06Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação de Mestrado_Gustavo Souza de Alencar e Silva.pdf: 4199856 bytes, checksum: 248a84b110ca0ac9a1ec5f9375ac6121 (MD5)eng
dc.description.provenanceMade available in DSpace on 2018-01-05T19:58:15Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação de Mestrado_Gustavo Souza de Alencar e Silva.pdf: 4199856 bytes, checksum: 248a84b110ca0ac9a1ec5f9375ac6121 (MD5) Previous issue date: 2016-12-15eng
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESpor
dc.formatapplication/pdf*
dc.languageporpor
dc.publisherUniversidade Federal de Alfenaspor
dc.publisher.departmentInstituto de Ciência e Tecnologiapor
dc.publisher.countryBrasilpor
dc.publisher.initialsUNIFAL-MGpor
dc.publisher.programPrograma de Pós-Graduação em Ciência e Engenharia de Materiaispor
dc.rightsAcesso Abertopor
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/-
dc.subjectMoagem de alta energia.por
dc.subjectMetais ceramicos.por
dc.subjectCarbonetos.por
dc.subjectSinterização.por
dc.subjectCarbonetos - Propriedades mecânicas.por
dc.subject.cnpqMATERIAIS NAO METALICOS::CERAMICOSpor
dc.titleSinterização por SPS de pós de W-C-CO-B preparados por moagem de alta energiapor
dc.title.alternativeSPS sintering of W-C-CO-B powders prepared by high energy millingeng
dc.typeDissertaçãopor
Aparece nas coleções:Mestrado

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Dissertação de Mestrado_Gustavo Souza de Alencar e Silva.pdfSinterização por SPS de pós de W-C-CO-B preparados por moagem de alta energia4,1 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Este item está licenciada sob uma Licença Creative Commons Creative Commons