Título: Incorporação de prata em vidros germanatos e teluritos contendo óxido de tântalo
Título(s) alternativo(s): Incorporation of silver in germanate and tellurite glasses containing tantalum oxide
Autor: RODRIGUES, Lais dos Santos 
Primeiro orientador: POIRIER, Gaël Yves
Primeiro coorientador: GIRALDI, Tânia Regina
Primeiro membro da banca: CASSANJES, Fabia Castro
Segundo membro da banca: PEREIRA, Camila
Resumo: O objetivo deste trabalho foi a preparação de vidros germanatos e teluritos contendo óxido de tântalo e a incorporação de prata nas matrizes, visando a caracterização da influência da prata nas propriedades ópticas e nos mecanismos de cristalização dos materiais. Foram preparados vidros nos sistemas (70-x)GeO2 – 10K2O – 20Ta2O5 – xAgNO3 e (80-x)TeO2 – 20(0,5Ta2O5) – xAgNO3, com x representando a proporção de nitrato de prata utilizado (%mol). As peças obtidas se mostraram homogêneas e com coloração amarelada para os dois sistemas. A utilização da técnica de calorimetria exploratória por DSC permitiu a determinação das temperaturas características das amostras (Temperatura de transição vítrea, Temperatura de início de cristalização e Temperarura de cristalização) e mostrou que a incorporação de prata na matriz vítrea favorece a precipitação de fases cristalinas em menores temperaturas. Tratamentos térmicos em temperaturas pré-estabelecida foram realizados a fim de avaliar a possibilidade de precipitação de prata nas matrizes vítreas, bem como a cristalização de fases óxidas. Os resultados obtidos não permitem afirmar que tenha ocorrido a precipitação de prata em nenhum dos sistemas vítreos, entretanto, foram obtidos resultados promissores para a amostra de Ge-05Ag, permitindo dizer que a composição utilizada possui alto potencial para a precipitação de NPs. Com relação aos vidros teluritos, o escurecimento homogêneo após o tratamento térmico das amostras pode estar relacionado à presença de nanopartículas de Ag precipitadas na matriz, ainda que com tamanhos maiores do que os esperados. As análises de DRX mostraram que não houve influência da prata no processo de cristalização do material.
Abstract: The purpose of this study was the preparation of germanate and tellurite glass containing tantalum oxide and the incorporation of silver on its matrixes, aiming at the characterization of the silver’s influence on the optical properties and on the crystallization mechanisms of the materials as well. The systems used for the glass’s preparation were (70-x)GeO2 – 10K2O – 20Ta2O5 – xAgNO3 e (80-x)TeO2 – 20(0,5Ta2O5) – xAgNO3, where x represents the silver nitrate proportion that was used (%mol). The pieces obtained appeared homogenous and yellowish for both systems. The use of the exploratory calorimetry through DSC technique allowed the characteristic temperature’s determination (Glass transition temperature, crystallization onset temperature and crystallization temperature) and showed that the incorporation of silver in the matrix favors the formation of the crystalline phase at lower temperatures. Thermal treatments at predefined temperatures were performed to evaluate the possibility of silver precipitation in the matrix, as well the crystallization of oxide phases. The results obtained do not allow to affirm that silver precipitation has occurred in any of the vitreous systems. However, promising results were obtained for the Ge-05Ag sample, allowing to say that the composition used has high potential for precipitation of NPs. Regarding glass tellurites, the homogeneous darkening after the samples thermal treatment may be related to the presence of precipitated Ag nanoparticles in the matrix, even with larger than expected sizes. The DRX analysis showed that there was no influence of silver on the material crystallization process.
Palavras-chave: Vidro.
Germânio.
Prata.
Tântalo.
Nanopartículas.
Área(s) do CNPq: ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS
Idioma: por
País: Brasil
Instituição: Universidade Federal de Alfenas
Sigla da instituição: UNIFAL-MG
Departamento: Instituto de Ciência e Tecnologia
Programa: Programa de Pós-Graduação em Ciência e Engenharia de Materiais
Citação: RODRIGUES, Lais dos Santos. Incorporação de prata em vidros germanatos e teluritos contendo óxido de tântalo. 2019. 62 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Alfenas, Poços de Caldas, 2019.
Tipo de acesso: Acesso Aberto
Endereço da licença: http://creativecommons.org/licenses/by-nc-nd/4.0/
URI: https://bdtd.unifal-mg.edu.br:8443/handle/tede/1529
Data de defesa: 27-Ago-2019
Aparece nas coleções:Mestrado
Mestrado

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Dissertação_LaisDosSantosRodrigues_2019_PPGCEM.pdfIncorporação de prata em vidros germanatos e teluritos contendo óxido de tântalo1,71 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Este item está licenciada sob uma Licença Creative Commons Creative Commons