Compartilhamento |
![]() ![]() |
Use este identificador para citar ou linkar para este item:
https://bdtd.unifal-mg.edu.br:8443/handle/tede/2422
Registro completo de metadados
Campo DC | Valor | Idioma |
---|---|---|
dc.creator | GIMENES, Bárbara Lavoura Dízero | - |
dc.contributor.advisor1 | SANFELICE, Rafaela Cristina | - |
dc.contributor.advisor1Lattes | http://lattes.cnpq.br/3030346954671333 | por |
dc.contributor.referee1 | MARINI, Juliano | - |
dc.contributor.referee2 | MAESTRELLI, Sylma Carvalho | - |
dc.date.accessioned | 2024-07-19T19:34:06Z | - |
dc.date.issued | 2024-01-19 | - |
dc.identifier.citation | GIMENES, Bárbara Lavoura Dízero. Estudo do potencial de reuso de aparas oriundas do processamento de malhas de sombreamento baseadas em polietileno. 2024. 76 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Alfenas, Poços de Caldas, MG, 2024. | por |
dc.identifier.uri | https://bdtd.unifal-mg.edu.br:8443/handle/tede/2422 | - |
dc.description.resumo | O uso cada vez mais frequente do plástico trouxe diversos benefícios para a humanidade devido à sua ampla versatilidade. No entanto, problemas decorrentes do descarte destes resíduos nos aterros sanitários e no meio ambiente tem levantado preocupações significativas. Esse estudo foca no Polietileno de Alta Densidade (PEAD), um polímero amplamente utilizado devido às suas propriedades notáveis, como resistência química e biológica e alta capacidade de moldagem, o que dificulta a ação de agentes naturais durante o processo de degradação, tornando necessário propor formas de reutilização desse material. Isso requer considerar objetivos econômicos (recursos e rentabilidade), sociais e ambientais. Nesse contexto, o objetivo central do estudo foi avaliar o potencial de reuso de aparas oriundas do processamento de malhas de sombreamento para uso agrícola fabricadas com polietileno (PE), de modo a validar o uso da opção sustentável. A análise abrangeu a caracterização estrutural, reológica, térmica e mecânica dos corpos de prova produzidos com o polietileno virgem (provindo direto da petroquímica), com o polietileno reciclado preto (obtido da reciclagem das malhas de sombreamento de PEAD de cor preta) e com o polietileno reciclado cinza (obtido por meio da reciclagem de mistura de malhas de sombreamento). Os resultados indicam que os materiais são similares quimicamente pois possuem bandas características de polietileno. Com relação a densidade, o PE reciclado preto apresentou valores típicos de PEAD (0,959 g/cm3 ), enquanto que o PE reciclado cinza apresentou valores típicos de PEBDL (0,932 g/cm3 ), reforçando a miscigenação de materiais de grade distinto de PE. Quanto às propriedades térmicas, evidenciou-se uma redução na temperatura de fusão para os reciclados (Tm = 125 a 128ºC), bem como uma ΔH indicando menor absorção e liberação de energia comparáveis ao virgem (Tm = 137ºC). Por fim, observou-se diferenças significativas nas propriedades mecânicas, sendo a amostra de polietileno virgem a de resistência à tração e módulo de Young superiores aos reciclados preto e cinza, com valores de 23,6 MPa, 19,9 MPa e 16,0 Mpa e 1109,5 MPa; 878,2 MPa e 390,7 Mpa, respectivamente, indicando uma maior capacidade de suportar cargas e manter a integridade estrutural. No entanto, evidenciou-se resultados inferiores do polietileno virgem em relação ao alongamento quando comparados aos materiais reciclados, cujos resultados foram 35,6%; 126,2% e 374,1%, sugerindo maior capacidade de deformação plástica antes do rompimento. Neste contexto, o reciclado preto apresentou potencial para reutilização na fabricação de malhas de sombreamento, embora requeira melhorias nas propriedades mecânicas para atender aos padrões de qualidade exigidos. Por outro lado, o reciclado cinza demonstrou ser proveniente de polietileno linear de baixa densidade devido a mistura de materiais, não tendo potencial para reuso nas malhas de sombreamento objeto do estudo. Por fim, este estudo ressalta a importância de considerar a sustentabilidade no ciclo de vida dos polímeros que resultam de aparas da indústria, destacando o potencial de reutilização destes através de reciclagem primária, contribuindo tanto para a economia circular quanto para a redução do impacto ambiental. | por |
dc.description.abstract | The increasingly frequent use of plastic has brought various benefits to humanity due to its wide versatility. However, problems arising from the disposal of these wastes in landfills and the environment have raised significant concerns. This study focuses on High Density Polyethylene (HDPE), a polymer widely used due to its remarkable properties, such as chemical and biological resistance and high molding capacity, which hinders the action of natural agents during the degradation process, making it necessary to propose ways to reuse this material. This requires considering economic (resources and profitability), social and environmental objectives. In this context, the central objective of the study was to evaluate the potential for reusing scraps from the processing of shading nets for agricultural use made with polyethylene (PE), in order to validate the use of the sustainable option. The analysis covered the structural, rheological, thermal and mechanical characterization of the test specimens produced with virgin polyethylene (coming directly from petrochemicals), with black recycled polyethylene (obtained from the recycling of black HDPE shading nets) and with gray recycled polyethylene (obtained by recycling a mixture of shade nets). The results indicate that the materials are chemically similar as they have characteristic polyethylene bands. Regarding density, black recycled PE presented typical HDPE values (0.959 g/cm3 ), while gray recycled PE presented typical LLDPE values (0.932 g/cm3 ), reinforcing the mix of grade materials other than PE. As for thermal properties, there was a reduction in the melting temperature for recycled materials (Tm = 125 to 128ºC), as well as a ΔH indicating lower absorption and release of energy comparable to virgin (Tm = 137ºC). Finally, significant differences were observed in the mechanical properties, with the virgin polyethylene sample having higher tensile strength and Young's modulus than the black and gray recycled ones, with values of 23.6 MPa, 19.9 MPa and 16.0 Mpa and 1109.5 MPa; 878.2 MPa and 390.7 Mpa, respectively, indicating a greater capacity to support loads and maintain the structural integrity. However, there were inferior results of virgin polyethylene in relation to elongation when compared to recycled materials, whose results were 35.6%; 126.2% and 374.1%, suggesting greater capacity for plastic deformation before failure. In this context, black recycled material showed potential for reuse in the manufacture of shading nets, although it requires improvements in mechanical properties to meet the required quality standards. On the other hand, the gray recycled material was shown to come from linear low-density polyethylene due to the mixture of materials and has no potential for reuse in the shading nets object of the study. Finally, this study emphasizes the importance of considering sustainability in the life cycle of polymers resulting from industrial scraps, highlighting the potential for reusing these through primary recycling, contributing both to the circular economy and to the reduction of environmental impact. | eng |
dc.description.provenance | Submitted by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2024-07-19T19:32:44Z No. of bitstreams: 1 Dissertacao_BárbaraLavouraDízeroGimenes_2024_PPGCEM.pdf: 1906248 bytes, checksum: b9f0fbb274513fb4ffed3e2ab900fc5a (MD5) | eng |
dc.description.provenance | Approved for entry into archive by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2024-07-19T19:33:15Z (GMT) No. of bitstreams: 1 Dissertacao_BárbaraLavouraDízeroGimenes_2024_PPGCEM.pdf: 1906248 bytes, checksum: b9f0fbb274513fb4ffed3e2ab900fc5a (MD5) | eng |
dc.description.provenance | Approved for entry into archive by Thaís Aparecida de Lima (thais.aplima@unifal-mg.edu.br) on 2024-07-19T19:33:32Z (GMT) No. of bitstreams: 1 Dissertacao_BárbaraLavouraDízeroGimenes_2024_PPGCEM.pdf: 1906248 bytes, checksum: b9f0fbb274513fb4ffed3e2ab900fc5a (MD5) | eng |
dc.description.provenance | Made available in DSpace on 2024-07-19T19:34:06Z (GMT). No. of bitstreams: 1 Dissertacao_BárbaraLavouraDízeroGimenes_2024_PPGCEM.pdf: 1906248 bytes, checksum: b9f0fbb274513fb4ffed3e2ab900fc5a (MD5) Previous issue date: 2024-01-19 | eng |
dc.format | application/pdf | * |
dc.language | por | por |
dc.publisher | Universidade Federal de Alfenas | por |
dc.publisher.department | Instituto de Ciência e Tecnologia | por |
dc.publisher.country | Brasil | por |
dc.publisher.initials | UNIFAL-MG | por |
dc.publisher.program | Programa de Pós-Graduação em Ciência e Engenharia de Materiais | por |
dc.rights | Acesso Aberto | por |
dc.subject | polietileno; | por |
dc.subject | aparas; | por |
dc.subject | malhas de sombreamento; | por |
dc.subject | reciclagem primária; | por |
dc.subject | polietileno de alta densidade. | por |
dc.subject.cnpq | MATERIAIS NAO METALICOS::POLIMEROS, APLICACOES | por |
dc.title | Estudo do potencial de reuso de aparas oriundas do processamento de malhas de sombreamento baseadas em polietileno | por |
dc.type | Dissertação | por |
Aparece nas coleções: | Mestrado |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Dissertacao_BárbaraLavouraDízeroGimenes_2024_PPGCEM.pdf | 1,86 MB | Adobe PDF | Baixar/Abrir Pré-Visualizar |